Important nonionic water-soluble polymer. High MW polymer is used primarily as a flocculant. Tg of high MW (>100,000) polymers = 165º. Unit weights are weights in solution.

10% soln. in water (25g polymer)

(Contains small amounts of formalin as fungicide)

Water-soluble all-primary polyamine.

Cationic polymer. Used to improve cell adhesion to solid surfaces.

0.1% soln. in water

Low molecular weight, water-soluble polymer. Forms insoluble polysalts with polyamines. Used as a pigment dispersant.

Water soluble carbohydrate with many pharmaceutical and technical uses.

Water soluble carbohydrate with many pharmaceutical and technical uses.

Water soluble carbohydrate with many pharmaceutical and technical uses.

Low molecular weight nonionic water-soluble polymer, used primarily as a flocculant. 50% solution in water. Unit weights are weights of solution.

Water-soluble cellulose ether, used as a binder and thickening agent

1,500-2,500 cps (1% soln. in water)

Water-soluble cellulose ether, used as a binder and thickening agent

Water-soluble polymer in a white, free flowing powder. Used to impart viscosity to and modify flow of aqueous solutions. See poly(ethylene glycol) for lower molecular weight analogs. Poly(ethylene glycol) has a broad molecular weight distribution ranging from~ 0.5x to 1.5x the values shown.

Soluble in: acetone, alcohol, chloroform, toluene, dichloromethane

PEO Contains 0.01% BHT, SiO₂ 1.5% max, alkaline earth oxide as CaO 0.5%,

Important anionic water-soluble polymer. Can be crosslinked covalently or ionically to form hydrogels.

Mw/Mn 2.4

63% soln. in water (157.5 g polymer)

Polymer is water-soluble at room temperature, insoluble above ~40º. Solubility ceiling has been used in mold and cell growth techniques since cells adhere to polymer film at incubation temperatures and are released as medium is cooled and polymer is dissolved.

Water-soluble resin of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydroyzed resin requiring onlyn 85°C for solution.

Soluble in: hot glycerol, hot glycols, hot water.

99.7 mol% hydrolyzed Polydispersity ~1.7

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

98 mol% hydrolyzed

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

80 mol% hydrolyzed

Important nonionic water-soluble polymer. High MW polymer is used primarily as a flocculant. Tg of high MW (>100,000) polymers = 165º. Unit weights are weights of solution.

Water-soluble anionic polymer. Has been used as a pigment dispersant.

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

98 mol% hydrolyzed

Water soluble cationic polymer with primary amino groups (free base types) for chemical reactions. High cationic charge density in ready to use aqueous solution form. The structure of these materials is a repeating polymer of the allyl amine group shown at right.

Ability to modify surfaces and provide cationic character allows the user to selectively attract negatively charged functional groups to the coated surface or to the dissolved water soluble cationic polymers.

Water-soluble polymer.

Soluble in: water, methanol, alkaline water.

Hydrophilic polymer, highly swolllen in water.

Water-soluble ionic polymer in salt form.

Polydispersity 3-5

Water-soluble ionic polymer in salt form.

Polydispersity 3-30

Water-soluble ionic polymer in acid form. (75g polymer)

Hydrophilic neutral polymer.

(30:70), 50% soln. in isopropanol (50g polymer)

Water sensitive resin, readily hydrolyzed. Used to prepare poly(vinyl alcohol) of varying degrees of hydrolysis.

Water-soluble polymer in a white, free flowing powder. Used to impart viscosity to and modify flow of aqueous solutions. See poly(ethylene glycol) for lower molecular weight analogs. Poly(ethylene glycol) has a broad molecular weight distribution ranging from~ 0.5x to 1.5x the values shown.

Soluble in: acetone, alcohol, chloroform, toluene, dichloromethane

PEO

Water-soluble polymeric phosphonic acid.

Polydispersity ~1.24

Water-soluble polymer in a white, free flowing powder. Used to impart viscosity to and modify flow of aqueous solutions. See poly(ethylene glycol) for lower molecular weight analogs. Poly(ethylene glycol) has a broad molecular weight distribution ranging from~ 0.5x to 1.5x the values shown.

Water-soluble polymer in a white, free flowing powder. Used to impart viscosity to and modify flow of aqueous solutions.

See poly(ethylene glycol) for lower molecular weight analogs. Poly(ethylene glycol) has a broad molecular weight distribution ranging from~ 0.5x to 1.5x the values shown.

Soluble in: acetone, alcohol, chloroform, toluene, dichloromethane

PEG

Water-soluble polymer in a white, free flowing powder. Used to impart viscosity to and modify flow of aqueous solutions. See poly(ethylene glycol) for lower molecular weight analogs. Poly(ethylene glycol) has a broad molecular weight distribution ranging from~ 0.5x to 1.5x the values shown.

Soluble in: acetone, alcohol, chloroform, toluene, dichloromethane

PEO

Tacky resin. Water-insoluble above 28º. Used to prepare heat-sensitive latex.

50% Aq. Soln.

Water-soluble surfactant.

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

99 mol% hydrolyzed Polydispersity ~2.4

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

88 mol% hydrolyzed Polydispersity ~1.9

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

Soluble in: hot glycerol, hot glycols, hot water.

88 mol% hydrolyzed Polydispersity ~2.0

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

99.7 mol% hydrolyzed Polydispersity ~1.7

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

88 mol% hydrolyzed Polydispersity ~1.9

Water-soluble polymeric phosphate ester. Uncrosslinked.

Phosphorous content min 5%

Water-soluble, photocrosslinkable polymer. Polymer has high dielectric constant. Commercially used for making screen-printing emulsions for direct and direct/indirect methods.

Other applications include non-silver films such as contact films, color proofing, deep-etch plates, color filters, suitable for UV curable films for biomedical coatings.

13.3% solution in water. 10g polymer PVA-SbQ 4.1 mol % SbQ

Hydrophilic polymer, more readily water-soluble than poly(2-hydroxyethyl methacrylate), in the presence of alkali, aqueous, 90% methanol.

Neutral, water soluble, polymer. Also soluble in DMF, lower alcohols, methyl ethyl ketone and methylene chloride. Tg = ~70º higher molecular weights.

Polydispersity ~3.4

Cationic quaternary ammonium polymer.

20% soln. in water (2g polymer) Degree of quaternization 50%

Cationic polymer. Used for promotion of cell adhesion to glass surfaces.

Water-soluble polymer used as a thickener, protective colloid.

Water-soluble polymer used as a thickener, protective colloid.

Polydispersity 3.6

Water-soluble polymer used as a thickener, protective colloid.

Polydispersity ~2.00

Water-soluble polymer used as a thickener, protective colloid.

Polydispersity 1.9

Cationic polymer. Used for promotion of cell adhesion to solid surfaces.

Water-soluble polymer used as a thickener, protective colloid.

Pharmaceutical grade

Polydispersity 3.33

Water-soluble at low pH has adhesive-promoting properties.

Water-soluble at low pH has adhesive-promoting properties.

Water-soluble cationic resin.

Water-soluble at low pH—has adhesive-promoting properties.

Water-soluble at low pH—has adhesive-promoting properties.

Water-soluble or water-dispersible polymers with surfactant properties. Chains are hydroxyl terminated. Polymers are p(EO/PO/EO) triblocks

ratio 0.15:1,

Water-soluble or water-dispersible polymers with surfactant properties. Chains are hydroxyl terminated. Polymers are p(EO/PO/EO) triblocks.

ratio 3:1