Powder with 40 micron average particle size. Soluble in DMF, DMAc, DMSO.

Powder with 40 micron average particle size. Soluble in DMF, DMAc, DMSO.

Reactive polymer capable of reacting at anhydride or backbone unsaturation.

125g polymer

Polymer reacts with amines, alcohols.

Polymer reacts readily with alcohols and amines. Can be used to prepare polymers bearing bioactive molecules. Firm, slightly tacky polymer. Can be transesterified or amidated readily.

2.5g polymer

Reactive polymer

2.5g polymer

Alternating copolymer, reactive with alcohols and amines. Hydrolyzes in water to a water-soluble anionic polymer.

Polymer is water-insoluble but water-swellable. Used as a hydrogel. See 2-hydroxyethyl methacrylate Soluble in: 95% lower alcohols (5% water), DMF

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

99 mol% hydrolyzed Polydispersity ~2.4

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

88 mol% hydrolyzed Polydispersity ~1.9

Water-soluble resin of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydroyzed resin requiring onlyn 85°C for solution.

Soluble in: hot glycerol, hot glycols, hot water.

99.7 mol% hydrolyzed Polydispersity ~1.7

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

98 mol% hydrolyzed

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

Soluble in: hot glycerol, hot glycols, hot water.

88 mol% hydrolyzed Polydispersity ~2.0

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

99.7 mol% hydrolyzed Polydispersity ~1.7

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

98 mol% hydrolyzed

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

88 mol% hydrolyzed Polydispersity ~1.9

Water-soluble resins of low toxicity. Resins at high % hydrolysis require heating at ~96°C in water for solution. Resins of lower % hydrolysis can be dissolved at progressively lower temperatures with 88% hydrolyzed resin requiring only 85°C for solution.

80 mol% hydrolyzed